3DO PA12 CF 0.8KG - Black Carbon Fiber
3DO PA12-CF is a carbon fiber-reinforced polyamide filament designed for industrial applications requiring maximum strength, stiffness, and dimensional stability. With excellent thermal resistance and low warping tendencies, it is ideal for weight-critical projects such as aerospace and motorsport.
A hardened nozzle is recommended due to the abrasive nature of the carbon fibers.
- Extremely high strength and stiffness
- High thermal resistance with a Vicat softening temperature of 145°C
- Lightweight, carbon fiber-reinforced for weight-critical projects
- Requires a hardened nozzle due to abrasive carbon fibers
- Nozzle: 260-290°C
- Heatbed: 110°C
Technical Specifications
Property | Test Method | Unit | Value |
---|---|---|---|
Density | ISO 1183 | g/cm³ | 1.03 |
Melt Volume Rate (MVR) 235°C/5.0 kg | ISO 1133 | cm³/10min | 7 |
Water Absorption (Saturation 23°C) | ISO 62 | % | 1.6 |
Tensile Modulus | ISO 527-1 | MPa | 2820 |
Tensile Strength | ISO 527-2 | MPa | 60.4 |
Tensile Elongation | ISO 527-2 | % | 4 |
Nominal Elongation at Break | ISO 527-2 | % | >35 |
Charpy Notched Impact Strength (+23°C) | ISO 179/1eA | kJ/m² | 9 |
Charpy Notched Impact Strength (-30°C) | ISO 179/1eA | kJ/m² | 5 |
Charpy Unnotched Impact Strength (+23°C) | ISO 179/1eU | - | No Break (NB) |
Charpy Unnotched Impact Strength (-30°C) | ISO 179/1eU | - | No Break (NB) |
Puncture Maximum Force (-30°C) | ISO 6603-2 | J | 62 |
Multiaxial Instrumented Impact Test, Peak Force -30°C | ISO 6603-2 | N | 5400 |
Heat Deflection Temperature (DTUL) 0.45 MPa, unannealed | ISO 75-2/B | °C | 139 |
Heat Deflection Temperature (DTUL) 1.8 MPa, unannealed | ISO 75-2/A | °C | 58 |
Vicat Softening Temperature | ISO 306/B50 | °C | 145 |
Mass Temperature | ISO 11357-3 | °C | 185 |
CLTE Flow | ISO 11359-2 | μm/m°C | 10 |
Specific Surface Resistance | IEC 60093 | ohms | 100 trillion (1 × 1014) |
Specific Volume Resistivity | IEC 60093 | ohms cm | 100 trillion (1 × 1014) |
Dielectric Strength | IEC 60243-1 | kV/mm | 25 |
Comparative Tracking Index (CTI) | IEC 60112 | V | 500 |